MS Polymer Sealant YN-M1507

Size: 280ml or 300ml/ Cartridge; 200L/Drum
Customization: OEM/ODM service available
Samples: provide free samples
Packing: 24 or 25 cartridges/carton;
600ml/sausage, 20 sausages/carton

Tel: +86-15966176633
Product Details

Products Description

YN-M1507 MS polymer sealant for HVAC pipeline is a one-component sealant based on high performance silicon modified polymers . Water absorption curing sealant . It is a general purpose industrial sealant, the products is developed and designed for general industrial materials, suitable for container, board room, van, bus, HVAC pipeline etc . industrial manufacturing industry general elastic sealing use.


1.Excellent weather resistance, suitable for all kinds of weather climate, more than 10 years serving life .
2.Green and environment, no odor, low VOC, very safe.
3.No shrink after curing, keep the original sealant shape.
4.Good adhesion to various substrates, suitable for carbon steel, stainless steel, aluminium, glass, paint layer etc.
5.Fast curing, can accelerate the projects progress. Better curing speed than other sealants in winter.


It is a universal elastic sealant with a wide range of uses.
It can form lasting adhesion and maintain elasticity to metal,plastic, wood, glass, ceramic, coating and other materials. It can be used indoors and outdoors and is suitable for elastic sealing of various joints.

Storage & Shelf Life

The shelf life is 9 months if stored in unopened-original package in a dry place at temperatures between +5℃ and +25℃.

Special Characteristics

1.Excellent weather resistance. Anti-UV, anti-ozone, can be used for internal and external sealing.
2.High-strength elastic bonding, used for board compounding and bonding of reinforcing ribs.
3.Long-term resistance to low temperature of -60 ℃ and high temperature of 90 ℃ .
4.Environmental protection, clean odor, harmful substances volatilized meet the requirements of national standard, European standard, and American standard.
Technical Date
Density1.55 + 0.03g/cm³
Skin time5-40min
Curing time≥2.5mm/24h
Elongation at break300%
Max tensile strength>1.8Mpa
100% Tensile strength>=0.8Mpa
Hardness Shore A35~45
Peel strength≥5.0 N/mm
Shrinkage rate after curing≤1.5%